The Product: Overview
  • TPO Resins
  • Cap Stock Resins (High Gloss)
  • Cap Stock Resins (Low Gloss)
    		•
    Technology: Overview
  • Technical Data Sheets
  • Guides
  • Sheet Extrusion
  • Thermoforming
  • General Painting
  • Repair (Painted)
  • Repair (Non Painted)
  • Bonding
  • Chemical Resistance
  • Labels/Decals
  • Welding
  • Troubleshooting
  • Project Support Services
    		•
    Press Releases

    Technical Data Sheets

    Invision® resins are based on enhanced polyolefin compositions that have been specifically designed to provide high melt strength for sheet and profile extrusion, and thermoforming applications. Invision resins can be categorized within the thermoplastic polyolefin (TPO) family of polymers. These resins provide many exciting benefits in performance and appearance compared to other commonly available resins. Pending your application requirements, a range of Invision TPO materials are available for use in monolayer sheet or as a substrate base for multilayer sheet structures which may utilize a co-extrusion of an Invision high and low gloss cap or color layer resin. Sheet products produced with Invision resins may consist of smooth or textured surfaces, in low or high gloss, and in mono or multi-layer structures.



    General Property Table - Invision® 1030 TPO
    Property Unit of Measure Typical Value
    Melt Flow Rate gm/10min
    230°C/2.16Kg    		 0.45
    Tensile at Yield psi
    (Mpa)    		 3365
    (23.2)
    Elongation at Break % 360
    Flexural Modulus psi
    (Mpa)    		 325,000
    (2241)
    Multi Axial Impact
    @ 5 mph (2.2 m/s)    		 in-lbs
    (Joules)    		 355
    (40.1)
    Impact Failure Mode Ductile/Brittle
    Failure Type    		 100% Ductile
    @ - 22°F
    (-30°C)
    Coefficient of Linear Thermal Expansion,
    - 30 °C to 80 °C,
    Value Shown x 10 -5    		 in/in/°F
    (in/in/°C)    		 2.33
    (4.2)
    Heat Distortion Test,
    66 psi (0.45Mpa) load
    *injection molded capstock resin    		 F
    (C)    		 223
    (106)
    Heat Sag, 8 inch span, two point,
    300 °F (149 °C) oven temperature    		 Inch
    (mm)    		 0
    (0)
    Density gm/ml 1.085
    Shrinkage after Forming, 24 hrs,
    Tool temp of 180° F (80° C)    		 % 0.7 - 0.9
    60 degree Gardner Gloss, Smooth Sheet,
    After Forming    		 % 40
    Maximum
    Download PDF Version of Table top


    General Property Table - Invision® 1040 TPO
    Property Unit of Measure Typical Value
    Melt Flow Rate gm/10min
    230°C/2.16Kg    		 0.5
    Tensile at Yield psi
    (Mpa)    		 3725
    (25.7)
    Elongation at Break % 323
    Flexural Modulus psi
    (Mpa)    		 400,000
    (2758)
    Multi Axial Impact
    @ 5 mph (2.2 m/s)    		 in-lbs (Joules) 449 (50.7)
    Impact Failure Mode Ductile/Brittle
    Failure Type    		 100% Ductile
    @ - 22°F
    (-30°C)
    Coefficient of Linear Thermal Expansion,
    - 30 °C to 80 °C,
    Value Shown x 10 -5    		 in/in/°F
    (in/in/°C)    		 2.33
    (4.2)
    Heat Distortion Test,
    66 psi (0.45Mpa) load
    *injection molded capstock resin    		 F
    (C)    		 237
    (114)
    Heat Sag, 8 inch span, two point,
    300 °F (149 °C) oven temperature    		 Inch
    (mm)    		 0
    (0)
    Density gm/ml 1.095
    Shrinkage after Forming, 24 hrs,
    Tool temp of 180° F (80° C)    		 % 0.7 - 0.9
    60 degree Gardner Gloss,
    Smooth Sheet, After Forming    		 % 40
    Maximum
    Download PDF Version of Table top


    General Property Table - Invision® 1050 TPO
    Property Unit of Measure Typical Value
    Melt Flow Rate gm/10min
    230°C/2.16Kg    		 0.5
    Tensile at Yield psi
    (Mpa)    		 3770
    (26)
    Elongation at Break % 230
    Flexural Modulus psi
    (Mpa)    		 475,000
    (3275)
    Multi Axial Impact
    @ 5 mph (2.2 m/s)    		 in-lbs
    (Joules)    		 386
    (43.6)
    Impact Failure Mode Ductile/Brittle
    Failure Type    		 100% Ductile
    @ - 5°F
    (-15°C)
    Coefficient of Linear Thermal Expansion,
    - 30 °C to 80 °C,
    Value Shown x 10 -5    		 in/in/°F
    (in/in/°C)    		 2.22
    (4.0)
    Heat Distortion Test,
    66 psi (0.45Mpa) load
    *injection molded capstock resin    		 F
    (C)    		 237
    (114)
    Heat Sag, 8 inch span, two point,
    300 °F (149 °C) oven temperature    		 Inch
    (mm)    		 0
    (0)
    Density gm/ml 1.14
    Shrinkage after Forming, 24 hrs,
    Tool temp of 180° F (80° C)    		 % 0.7 - 0.9
    60 degree Gardner Gloss,
    Smooth Sheet, After Forming    		 % 40
    Maximum
    Download PDF Version of Table top


    General Property Table - Invision® 1060 TPO
    Property Unit of Measure Typical Value
    Melt Flow Rate gm/10min
    230°C/2.16Kg    		 0.7
    Tensile at Yield psi
    (Mpa)    		 4465
    (30.8)
    Elongation at Break % 175
    Flexural Modulus psi
    (Mpa)    		 580,000
    (4000)
    Multi Axial Impact
    @ 5 mph (2.2 m/s)    		 in-lbs
    (Joules)    		 360
    (40.7)
    Impact Failure Mode Ductile/Brittle
    Failure Type    		 100% Ductile
    @ 40°F
    (5°C)
    Coefficient of Linear Thermal Expansion,
    - 30 °C to 80 °C,
    Value Shown x 10 -5    		 in/in/°F
    (in/in/°C)    		 2.98
    (5.36)
    Heat Distortion Test,
    66 psi (0.45Mpa) load
    *injection molded capstock resin    		 F
    (C)    		 242
    (117)
    Heat Sag, 8 inch span, two point,
    300 °F (149 °C) oven temperature    		 Inch
    (mm)    		 0
    (0)
    Density gm/ml 1.16
    Shrinkage after Forming, 24 hrs,
    Tool temp of 180° F (80° C)    		 % 0.7 - 0.9
    60 degree Gardner Gloss,
    Smooth Sheet, After Forming    		 % 40
    Maximum
    Download PDF Version of Table top


    General Property Table - Invision® 3566 Cap & Color Resin
    Property Unit of Measure Typical Value
    Melt Flow Rate gm/10min
    230°C/2.16Kg    		 4
    Tensile at Yield psi
    (Mpa)    		 4350
    (30)
    Elongation at Break % n/a
    Flexural Modulus psi
    (Mpa)    		 145,000
    (1000)
    Multi Axial Impact @ 5 mph
    (2.2 m/s)    		 in-lbs
    (Joules)    		 n/a
    Impact Failure Mode Ductile/Brittle
    Failure Type    		 n/a
    Coefficient of Linear Thermal Expansion,
    - 30 °C to 80 °C,
    Value Shown x 10 -5    		 in/in/°F
    (in/in/°C)    		 n/a
    Heat Distortion Test,
    66 psi (0.45Mpa) load
    *injection molded capstock resin    		 F
    (C)    		 167
    (75)
    Heat Sag, 8 inch span, two point,
    300 °F (149 °C) oven temperature    		 Inch
    (mm)    		 n/a
    Density gm/ml .90
    Shrinkage after Forming, 24 hrs,
    Tool temp of 180° F (80° C)    		 % n/a
    60 degree Gardner Gloss,
    Smooth Sheet, After Forming    		 % 85
    Minimum
    Download PDF Version of Table top


    General Property Table - Invision® 3567 Cap & Color Resin
    Property Unit of Measure Typical Value
    Melt Flow Rate gm/10min
    230°C/2.16Kg    		 3
    Tensile at Yield psi
    (Mpa)    		 6105
    (42.1)
    Elongation at Break % n/a
    Flexural Modulus psi
    (Mpa)    		 300,000
    (2070)
    Multi Axial Impact
    @ 5 mph (2.2 m/s)    		 in-lbs
    (Joules)    		 n/a
    Impact Failure Mode Ductile/Brittle
    Failure Type    		 n/a
    Coefficient of Linear Thermal Expansion,
    - 30 °C to 80 °C,
    Value Shown x 10 -5    		 in/in/°F
    (in/in/°C)    		 n/a
    Heat Distortion Test,
    66 psi (0.45Mpa) load
    *injection molded capstock resin    		 F
    (C)    		 264
    (129)
    Heat Sag, 8 inch span, two point,
    300 °F (149 °C) oven temperature    		 Inch
    (mm)    		 n/a
    Density gm/ml .90
    Shrinkage after Forming, 24 hrs,
    Tool temp of 180° F (80° C)    		 % n/a
    60 degree Gardner Gloss,
    Smooth Sheet, After Forming    		 % 85
    Minimum
    Download PDF Version of Table top


    General Property Table - Invision® 3568 Cap & Color Resin
    Property Unit of Measure Typical Value
    Melt Flow Rate gm/10min
    230°C/2.16Kg    		 0.7
    Tensile at Yield psi
    (Mpa)    		 2400
    (16.6)
    Elongation at Break % 390
    Flexural Modulus psi
    (Mpa)    		 40,000
    (276)
    Multi Axial Impact
    @ 5 mph (2.2 m/s)    		 in-lbs
    (Joules)    		 n/a
    Impact Failure Mode Ductile/Brittle
    Failure Type    		 100% Ductile
    @ - 40° F
    (- 40° C)
    Coefficient of Linear Thermal Expansion,
    - 30 °C to 80 °C,
    Value Shown x 10 -5    		 in/in/°F
    (in/in/°C)    		 n/a
    Heat Distortion Test,
    66 psi (0.45Mpa) load
    *injection molded capstock resin    		 F
    (C)    		 140
    (60)
    Heat Sag, 8 inch span, two point,
    300 °F (149 °C) oven temperature    		 Inch
    (mm)    		 n/a
    Density gm/ml .89
    Shrinkage after Forming, 24 hrs,
    Tool temp of 180° F (80° C)    		 % 1.2-1.6
    60 degree Gardner Gloss,
    Smooth Sheet, After Forming    		 % 20
    Maximum
    Download PDF Version of Table top


    General Property Table - Invision® 3570 Cap & Color Resin
    Property Unit of Measure Typical Value
    Melt Flow Rate gm/10min
    230°C/2.16Kg    		 0.79
    Tensile at Yield psi
    (Mpa)    		 2379
    (16)
    Elongation at Break % 342
    Flexural Modulus psi
    (Mpa)    		 128,213
    (884)
    Multi Axial Impact
    @ 5 mph (2.2 m/s)    		 in-lbs
    (Joules)    		 n/a
    Impact Failure Mode Ductile/Brittle
    Failure Type    		 n/a
    Coefficient of Linear Thermal Expansion,
    - 30 °C to 80 °C,
    Value Shown x 10 -5    		 in/in/°F
    (in/in/°C)    		 n/a
    Heat Distortion Test,
    66 psi (0.45Mpa) load
    *injection molded capstock resin    		 F
    (C)    		 122.4
    (50.2)
    Heat Sag, 8 inch span, two point,
    300 °F (149 °C) oven temperature    		 Inch
    (mm)    		 n/a
    Density gm/ml .93
    Shrinkage after Forming, 24 hrs,
    Tool temp of 180° F (80° C)    		 % n/a
    60 degree Gardner Gloss,
    Smooth Sheet, After Forming    		 % 75
    Minimum
    Download PDF Version of Table top

    At a Glance (TPO)

    Property Unit Of
    Measure         		Typical Value
    Invision®
    1030 TPO    		 Invision®
    1040 TPO    		 Invision®
    1050 TPO    		 Invision®
    1060 TPO
    Melt Flow Rate gm/10min
    230°C/2.16Kg     		0.45 0.5 0.5 0.7
    Tensile at Yield psi
    (Mpa)     		3365
    (23.2)     		3725
    (25.7)     		3770
    (26)     		4465
    (30.8)
    Elongation at Break % 360 323 230 175
    Flexural Modulus psi
    (Mpa)     		325,000
    (2241)     		400,000
    (2758)     		475,000
    (3275)     		580,000
    (4000)
    Multi Axial Impact
    @ 5 mph (2.2 m/s)     		in-lbs
    (joules)     		355
    (40.1)     		449
    (50.7)     		386
    (43.6)     		360
    (40.7)
    Impact Failure
    Mode @ 5 mph,
    (2.2 m/s)     		Ductile/Brittle
    Failure Type     		100% Ductile
    @ - 22°F
    (-30°C)     		100% Ductile
    @ - 22°F
    (- 30°C)     		100% Ductile
    @ - 5°F
    (- 15°C)     		100% Ductile
    @ 40°F
    (5°C)
    Coefficient of Linear
    Thermal Expansion,
    - 30 °C to 80 °C,
    Value Shown x 10 -5     		in/in/°F
    (in/in/°C)
    (mm/mm/°C)     		2.33
    (4.2)     		2.33
    (4.2)     		2.22
    (4.0)     		2.98
    (5.36)
    Heat Distortion Test,
    66 psi (0.45 Mpa) load
    *(injection molded capstock resin)     		°F
    (°C)     		223
    (106)     		237
    (114)     		237
    (114)     		242
    (117)
    Heat Sag, 8 inch
    span, two point,
    300°F (149° C)
    Oven temperature     		inch
    (mm)     		0
    (0)     		0
    (0)     		0
    (0)     		0
    (0)
    Density gm/ml 1.085 1.095 1.14 1.16
    Shrinkage after
    Forming, 24 hrs, Tool
    temp of 180° F (80° C)     		% 0.7-0.9 0.7-0.9 0.7-0.9 0.7-0.9
    60 degree Gardner
    Gloss, Smooth Sheet, After Forming     		% 40
    Maximum     		40
    Maximum     		40
    Maximum     		40
    Maximum
    Download PDF Version of TPO and Cap & Color Resin Tables top

    At a Glance (Cap & Color Resin)

    Property Unit Of
    Measure         		Typical Value
    Invision®
    3566 Cap & Color Resin    		 Invision®
    3567 Cap & Color Resin    		 Invision®
    3568 Cap & Color Resin    		 Invision®
    3570 Cap & Color Resin
    Melt Flow Rate gm/10min
    230°C/2.16Kg     		4 3 0.7 0.79
    Tensile at Yield psi
    (Mpa)     		4350
    (30)     		6105
    (42.1)     		2400
    (16.6)     		2379
    (16)
    Elongation at Break % n/a n/a 390 342
    Flexural Modulus psi
    (Mpa)     		145,000
    (1000)     		300,000
    (2070)     		40,000
    (267)     		128,213
    (884)
    Multi Axial Impact
    @ 5 mph (2.2 m/s)     		in-lbs
    (joules)     		n/a n/a n/a n/a
    Impact Failure
    Mode @ 5 mph,
    (2.2 m/s)     		Ductile/Brittle
    Failure Type     		n/a n/a 100% Ductile
    @ - 40°F
    (- 40°C)     		n/a
    Coefficient of Linear
    Thermal Expansion,
    - 30 °C to 80 °C,
    Value Shown x 10 -5     		in/in/°F
    (in/in/°C)
    (mm/mm/°C)     		n/a n/a n/a n/a
    Heat Distortion Test,
    66 psi (0.45 Mpa) load
    *(injection molded capstock resin)     		°F
    (°C)     		167
    (75)     		264
    (129)     		140
    (60)     		122.4
    (50.2)
    Heat Sag, 8 inch
    span, two point,
    300°F (149° C)
    Oven temperature     		inch
    (mm)     		n/a n/a n/a n/a
    Density gm/ml 0.90 0.90 0.89 0.93
    Shrinkage after
    Forming, 24 hrs, Tool
    temp of 180° F (80° C)     		% n/a n/a 1.2-1.6 n/a
    60 degree Gardner
    Gloss, Smooth Sheet, After Forming     		% 85
    Minimum     		40
    Minimum     		20
    Maximum     		75
    Minimum
    Download PDF Version of TPO and Cap & Color Resin Tables top